FLEXICLAD® ER

Revolutionary Elastomeric Polymer Composite Repairs, Resurfaces & Protects Flexible Components.

FLEXICLAD ER is a two component, 100% solids, trowelable polymer composite that has been specifically formulated to repair damaged flexible components such as conveyor belts, hoses, off-road tire sidewalls, etc.

FLEXICLAD ER is a very unique material that requires no primer, bonds to most rubber / flexible materials and cures at ambient temperatures – no heat is required. It is safe and simple to use and no special tools are needed. It can be used to create irregular flexible gaskets on distorted flange faces or to create a resilient bond for metal, wood, etc. It can also be used to seal / caulk heat exchanger water boxes to tube sheet faces or to seal joints in condensate pans, cooling tower pans, etc. FLEXICLAD ER is an indispensable addition to any maintenance engineer’s tool box.

FLEXICLAD ER is ideal for sealing joints and seams on machinery and equipment that are prone to vibration or movement – and wherever flexible repairs are required:


Technical Data

Volume capacity per 250 g unit
14.1 in3 / 233 cm3
Mixed density
0.039 lbs per in3 / 1.07 gm per cc
Coverage rate per 250 g unit @ 1/8 inch
113 in2 / 730 cm2
Shelf life
Indefinite
Volume Solids
100%
Mixing ratio Base Activator
By Volume 1
By Weight 1.8 1

Working Life and Cure Times

Ambient Temperature Working Life Return to Service Full Cure
41°F 5°C 50 min. 8 hrs. 5 days
59°F 15°C 30 min. 6 hrs. 4 days
77°F 25°C 16 min. 3 hrs. 3 days
86°F 30°C 12 min. 45 min. 36 hrs.

Physical Properties

Typical Values Test Method
Hardness - Shore D 15 ASTM D-2240
Elongation 175%   ASTM D-2370
Tensile Shear Adhesion
Steel 500 psi 35 kg/cm2 ASTM D-1002
Copper 500 psi 35 kg/cm2 ASTM D-1002
Both cases exhibited cohesive failure in the FLEXICLAD® ER itself.
Note: Adhesion to most rubber substrates when properly prepared is greater than the cohesive strength of the rubber substrate.

Chemical Resistance

Acetic acid (10%) G Nitric acid (0-10%) G
Aviation fuel G Phosphoric acid (0-5%) EX
Butyl alcohol G Phosphoric acid (5-10%) G
Calcium chloride EX Potassium chloride EX
Crude Oil EX Propyl alcohol G
Diesel fuel EX Sodium chloride EX
Ethyl alcohol G Sodium hydroxide EX
Gasoline G Sulfuric acid (0-10%) EX
Hydrochloric acid (0-10%) EX Sulfuric acid (10-20%) G
Hydrochloric acid (10-20%) G    

EX - Suitable for most applications including immersion
G - Suitable for intermittent contact, splashes, etc.

Extended Information

Ask an ENECON Tech

Fill out my online form.

Sign up for ENECON's latest Repair - Don't Replace solution

Fill out my online form.